Composite membranes based on geometrically constrained PIM-1 for dehumidification of gas mixtures

E. A. Chernova, I. V. Roslyakov, S. G. Dorofeev, A. V. Lukashin

Lomonosov Moscow State University, Leninskiye Gory, Moscow, 119991, Russia

Аннотация: Composite membranes based on polymer with intrinsic microporosity (PIM-1) confined in the pores of porous anodic alumina (AAO) supports were prepared by spin-coating method under vacuum suction. Water permeance of the membranes was measured at humidities ranging from 10 to 70%. High permeance towards water vapors reaching the value of $\sim$ 13700 l/(m$^2\cdot$bar$\cdot$h) coupled with the H$_2$O/N$_2$ selectivity of 1400 was observed at the humidity of 70% for composite membranes due to the condensation in nanopores of polymer and anodic alumina channels. The obtained selectivity exceeds strongly that of bulk PIM-1 due to confinement of polymer chains mobility in AAO channels. The water vapor sorption capacity for composite membranes exceeds 7% being governed both by condensation in polymer micropores and anodic alumina channels. Physical ageing of the membranes was monitored for a period of 6 months and then the membranes were subjected to activation in methanol. It was established that physical ageing substantially reduces the water permeance but activation in methanol allows one to partially rejuvenate water transport performance.

Ключевые слова: dehumidification, polymer with intrinsic microporosity, geometric confinement, physical ageing.

PACS: 81.05.Rm, 47.56.+r

Поступила в редакцию: 16.05.2019
Исправленный вариант: 25.05.2019

Язык публикации: английский

DOI: 10.17586/2220-8054-2019-10-3-282-288



Реферативные базы данных:


© МИАН, 2024