Abstract:
Comparative analysis of the influence of temperature and laser activation on the secondary electron emission coefficient and work function $(e\varphi)$ in Pd–Ba alloy (1.5 at % Ba) has been conducted. The optimum density of laser radiation has been shown to roughly equal 2 J/cm$^2$. Reasons why the emission efficiency of Pd–Ba alloy decreases after long-term heating have been found.
Keywords:metal alloy, emission properties, temperature annealing, laser activation, secondary electron emission coefficient, work function, topography, emission efficiency.