Abstract:
The goal of this study was the sol-gel synthesis of nanocrystals La$_{1-x}$Sr$_{x}$FeO$_{3}$ (x = 0.0, 0.1, 0.2, 0.3) and an examination of their magnetic properties. An aqueous solution of ammonia and 5% ammonium carbonate solution were used as precipitating agents. It was established that the crystallization of LaFeO$_{3}$ is completed at 750$^\circ$C (annealing for 1 h). The average diameter of the synthesized particles was 80–100 nm. Investigation of the magnetic properties showed non-monotonic changes of saturation magnetic moment and increase of coercive force with increased Sr content in the sample.
Keywords:sol-gel synthesis, nanopowders, lanthanum ferrite, magnetic properties, high-coercivity materials.