Наносистемы: физика, химия, математика, 2017, том 8, выпуск 4, страницы 512–522 (Mi nano68)

CHEMISTRY AND MATERIAL SCIENCE

Sizes and size distributions of nanoparticles: Causes of differences in results obtained by transmission electron microscopy and small angle X-ray scattering

D. O. Shvedchenko, V. V. Volkov, E. I. Suvorova

A.V. Shubnikov Institute of Crystallography of Russian Academy of Sciences, Leninsky pr., 59, 119333 Moscow, Russia

Аннотация: Comparative size and structure characterization of silver and selenium nanoparticles obtained and stabilized in different polymer solutions was performed by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS). Effects of instrumental properties, nature of the samples, data collecting and data processing on accuracy of measurements are highlighted and summarized. Numerical differences in the mode diameter values derived from the TEM and SAXS data were found to have different sources. The SAXS results can be misleading in case of small particles (2–4 nm), for instance, Ag nanoparticles formed and stabilized in some aqueous polymer solutions due to instrumental limits, while TEM can provide sufficient statistics on such nanoparticles. SAXS is efficient in characterization of size distributions for soft Se-polymer composite particles of 20 to 100 nm in diameter. TEM is mandatory for investigating the chemical and phase composition of particles in mixtures, and their formation mechanism.

Ключевые слова: nanoparticles, selenium, silver, transmission electron microscopy, small-angle X-ray scattering, size distribution.

PACS: 61.05cf + 61.46.Df + 68.37.Lp

Поступила в редакцию: 26.07.2017
Исправленный вариант: 05.08.2017

Язык публикации: английский

DOI: 10.17586/2220-8054-2017-8-4-512-522



Реферативные базы данных:


© МИАН, 2024